| Polymer performance/type | Unit | PEEK5600CF30 | Testing standards |
| Carbon fiber content 30% | 30% carbon fiber | —— | |
| Tensile strength | MPa | 220 | ISO 527-1/-2 |
| Tensile modulus | GPa | 21 | ISO 527-1/-2 |
| Elongation at break | % | 1.7 | ISO 527-1/-2 |
| Bending strength | MPa | 321 | ISO 178 |
| Bending modulus | GPa | 17.9 | ISO 178 |
| Notched impact strength | J/m | 637 | ISO 180/IU |
| Hot deformation temperature 1.82MPa | ℃ | 315 | ISO 75-1/-2 |
| Linear thermal expansion coefficient flow direction | ppm/℃ | 7 | ISO 11359-1/-2 |
| Linear coefficient of thermal expansion in the transverse direction | ppm/℃ | 56 | ISO 11359-1/-2 |
| Water absorption rate24h | % | 0.1 | ISO 62 |
| Proportion | g/cm³ | 1.41 | ISO 1183 |